Calcium Polysulphide as a Sulfidizator at Flotation of the Oxidized Lead–Bearing Ores

More complex and heavy-concentrating oxidized and mixed sulphidic oxidized ores are involved in production because of increasing needs for non-ferrous metals. Extraction of the oxidized minerals of non-ferrous metals general in current technologies. The problem is solved to oxidized polymetallic ores the preliminary selective sulphidization is the oxidized surface of the components by means of hydrogen sulphide, sulphide and calcium polysulphide, and also element sulphur, etc. The task was to study details of flotation of the oxidized lead-bearing ore of the Zarechnoe deposit (Kazakhstan) with calcium polysulphide as sulphidation. According to chemical analysis initial samples of the ore contain, %: lead – 4.8; zinc – 0.1; general iron – 0.81. Phase structure lead is characterized by the oxidized form of 57.76-64.5 %; by sulphidic status of 25.5-32.64 %, and by plyumboyarosite of 19.0-23.02 %. Researches on flotation beneficiation of oxidized lead-bearing ore are conducted. Sulfidizator gave to grinding, on flotations there were used the collector (butyl xanthogenate of sodium) and frother (T-80). Experiments were conducted with a new sulphidizator – calcium polysulphide. The latter is obtained by interaction of CaO calcium oxide with sulfur and water at high temperature with component mass the following ratio S:CaO:H2O =10:5:85. Extent of mill initial ore was optimised (88.42 % of - 0.071 mm grade). For the optimum mill mode the studies on matching of an optimized consumption of sulphidizators are performed. On basic technology with application of sulphide of sodium as a sulphidizator at optimum mill, the lead concentrate with the content of lead 64.4 % at extraction of 86.6 % was received. The content of cerussite in a concentrate was about 14.9 % at extraction of 82.1 %. With application of calcium polysulphide as a sulphidizator the lead concentrate with the content of lead 68.0 % at extraction of 88.0 % was received. The content of cerussite has made 16.0 % at extraction of 85.0 %. Application of a new sulphidizator allows to increase extraction of lead in a concentrate from 64.4% to 68% and cerussite extraction – from 82.1 % to 85.0 %. The possibility of application of calcium polysulphide as a sulphidizator instead of conventional sulphurous sodium was established.