Characteristics and Non-Isothermal Crystallization Kinetics of Spinels in Vanadium Slag Containing High Content of Chromium

"Hongge Ore, a kind of vanadium-titanium magnetite ore containing high content of chromium, is valuable resource for extracting Fe, V and Cr in China. During present processing of the ore, vanadium and chromium were both concentrated in slag, leading to higher content of chromium in the vanadium slag than that of common one in Pan-Steel. Mineral phases and characteristics of spine! crystals, which influenced greatly subsequent roasting process, in the vanadium slag under different cooling conditions were investigated by using XRD and SEM/EDS. Results showed that vanadium slags containing various contents of chromium were composed of spine!, in which V and Cr were both concentrated, olivine and pyroxene. Growth rate of spine ls decreased sharply below 1350°C. The non-isothermal crystallization process could be described by modified Avrami equation and Ozawa equation. Avrami exponent and Ozawa index were calculated and growth mechanism of spine! crystals was discussed.IntroductionVanadium (V) as well as chromium (Cr) is important non-ferrous metal widely used in materials and chemical industries [1, 2]. Especially, both of them are important alloying elements for the production of high alloyed steels to achieve desired physical-chemical and mechanical properties. Vanadium-titanium magnetite ore in Panzhihua-Xichang area (China) is an important raw material for extracting vanadium. During the extracting process, vanadium is firstly reduced into hot metal and then concentrated in slag phase by blowing oxygen into the hot metal in converter [3]. This kind of slag containing 5~20 wt% V20 3 are usually roasted with sodium or calcium salts and then leached to obtain vanadium containing solution and final products. Current vanadium slag obtained from normal vanadium-titanium magnetite ore contains low content of Cr20 3 and chromium extraction is thus ignored. However, chromium content in the vanadium slag would be increased intensively when the Hongge Ore used, which is also important vanadium titanium magnetite in Panzhihua-Xichang area containing 0.2~0.8 wt% Cr203. Therefore, this kind of vanadium slag with high content of chromium would also be important sources for vanadium and chromium extraction. According to previous work [4], both vanadium and chromium could be extracted from vanadium slag with high content of chromium by salt roasting and leaching, which is illustrated in Fig.1."