Coating Characterization in CRN Deposited by Magnetron Sputtering Method on AISI 316 Steel (930e619a-a842-413e-ab40-0890c04eefce)

"Chromium Nitride (CrN) thin fihns were deposited on steel AISI 316 substrates with reactive magnetron sputtering method. CrN films were produced under two different conditions. In the first one, the substrate was heated by a d.c. source. At the second coating was applied a negative substrate bias voltage. X ray diffraction, quantitative energy dispersive and scanning electron microscope, were employed to characterize their phases, chemical composition and microstructure. Additionally microhardness was evaluated using a microhardness tester. The results show that the phase formation of CrN thin films in the first case (with temperature) is better. Both coatings presented homogeneous surface. Their compositions shows differences though that gases flow are same. In attention to their hardness, presents an increment if it's compared with hardness substrate.Nomenclature.P Ar =Argon gas pressure during coating.PN2 = Nitrogen gas pressure during coating.Ts = Substrate temperature during coating.T f = Coating melting temperature. (CrN = 1050°C).E=Potential difference.t =Coating time.P=Target power (Cr) in magnetron sputtering de.HV = Vickers hardness.F = Applied charge.d= Average length of longitude of the two diagonals (mm)Introduction.Wear causes losses in materials surface, generating that components of mechanical systems suffer irreversible changes in their properties, causing a faulty operation of the system. It is important to control their effects, measuring and interpreting their causes clearly."