Damping Behaviour of Alminite Particulate Reinforced ZA-27 Alloy Metal Matrix Composites

"Damping behaviour of aluminite particulate reinforced ZA-27 alloy metal matrix composites processed by compocasting method is studied. The weight percentage of particulate reinforcement is 0,1,2,3, and 4%. A dynamic mechanical· analyzer is used ·to measure the damping capacity and dynamic modulus at the natural frequency of the specimen over a temperature range of 30°C to 300 °C both in the heating and cooling cycle. The damping capacity of the material is found to increase with increase in temperature and weight percentage of aluminite reinforcement although this is accompanied by a decrease in dyliamic modulus.The damping capacity and dynamic young's modulus exhibit a sharp decrease in their values around 300 °C a8 ZA-27 alloy undergoes a first order phase transition in this region which is confirmed by Differential scanning calorimetric studies. Several damping mechanisms have been evaluated theoretically for the material under study. The damping capacity at low temperatures is attributed primarily to coefficient of thermal expansion mismatch induced dislocations and high intrinsic damping of the matrix. At higher temperatures the damping capacity is attributed to ZA-27/aluminite interface, phase transformations and thermoelastic damping.IntroductionMetal matrix composites. (MMCs) offer designers many added benefits, as they are particularly suited for applications requiring good strength at high temperature, good structural rigidity, dimensional stability, and lightweight [1-5]. At present, the usage of ceramic particles as reinforcement in MMCs has attracted considerable interest from scientists and engineers. The MMCs show substantially improved elastic modulus, strength, stiffiless, and tribological properties with low coefficient of thermal expansion compared with the unreinforced matrix material."