Dezincing of Iron-Containing Secondary Raw Materials in Frothed Slag Layer in an Electric DC Arc Furnace

The proposed process is based on creating a controlled frothed layer of molten slag, in which fine particles of carbonaceous reductant and raw material to be processed are mixed with emulsified iron. Frothing of the slag layer without external blowing occurs as a result of intensive evolution of gaseous reduction products. The froth reaction process is maintained due to the heat of an electric arc in the slag layer. When the metal bath is heated by the arc to 1400- 1 500°C, the low temperature of the slag surface of about 1200-1 300°C is maintained due to low thermal conductivity of slag froth preventing heat loss. In order to maintain the required slag froth level and control the process temperature, air tuyeres are installed above the slag bath; blowing air serves also for oxidation of zinc in fumes and for its transportation. High adsorption and thermal insulating properties of slag froth ensure virtually complete elimination of dust and mist entrainment along with low heat losses. The main macrokinetic regularities of the carbon thermal reduction of zinc-containing slag melts have been studied under frothing conditions. The mechanism of formation of gas-slag emulsion has been identified under the conditions of reaction [C]+[O]=CO occurring locally at the slag-metal interface. It has been demonstrated that under the froth reduction conditions the zinc removal rate from the melt increases on the average by 3 to 5 times. Based on the physical and chemical data obtained, basic principles of the dezincing technology have been developed for different intermediate oxide iron-containing products produced in the process of ferrous and non-ferrous metals production.