Discussion - In-Place Leaching at Miami Mine, Miami, Arizona – Transactions SME/AIME, Vol. 250, No. 4, December 1971, pp. 310-314 – Fletcher, James B.

Harmon E. Keyes (Chemical & Metallurgical Engineer, Eagar, Ariz.)-Chemical dissolution of chalcocite by acidic ferric sulfate is well known. Resulting elemental sulfur may be oxidized to sulfuric acid by heated ferric sulfate. Laboratory tests at Southwest Experiment Station, USBM, Tucson, generally confirmed stoichiometric relations of 1 part Cu dissolved to 1.750 parts ferric iron reduced, using CP chemicals, dried ore samples, and apparatus cleaned with potable water. Recirculation with open-drainage percolation to increase copper in leaching solvent was followed successfully when appropriate, both in laboratory and Pinto Valley pilot tests. Before 1924 attempts to produce ferric sulfate by aerating ferrous sulfate solution were known. Initial oxidation was satisfactory, but rate slowed below practicality as oxidation progressed and acidity increased. Also, due to hydrolysis of ferric sulfate, a ferric precipitate of hydroxide and basic sulfate resulted. Both laboratory and pilot plant tests gave similar results, regardless of whether CP ferrous sulfate or scrap iron cementation discard solution was used. Rapid oxidation of ferrous hydroxide by air alone is well known to analytical chemists. I demonstrated a process to produce acidic ferric sulfate solutions by precipitating ferrous hydroxide with milk of lime, aerat-