Effect Of Additives On Phase Transformation Of Nickel Laterite Ore During Low-Temperature Reduction Roasting Process Using Carbon Monoxide

The effects of additives with Na2S, Na2SO4 and CaSO4 on phase transformation of nickel laterite ore in low-temperature reduction roasting process using carbon monoxide were investigated. The results showed that diffraction peaks of forsterite increased with increasing reduction temperature for 30min with the addition of 10wt% Na2SO4 and 50vol% CO, and diffraction peaks of forsterite increased with increasing the content of Na2SO4 at 900°C for 30min. Comparing the above three additives, phase transformation of nickel laterite ore were strongly influenced with the addition of 10 wt% Na2SO4 and 10 wt% Na2S. Calcium sulphide from the thermal decomposition of CaSO4 was carried out in the reaction product. SEM-EDS analysis result deduced that increasing the dosage of Na2SO4 from 10wt% to 15wt% could promote the polymerization of ferronickel and improve the grade of nickel in ferronickel.