Effect of Argon Gas Purging of Spark Plasma Sintered ZrB2+SiC Nano-Powder Composites

Spark Plasma Sintering (SPS) consolidated ZrB2+SiC composites using nano-powders (around 40 nm) showed smaller grains compared to those using micron size powders and segregation of SiC into islands is minimal but with higher oxidation of ZrB2 to form ZrO2 in nano-composites. Argon-gas purging prior to SPS consolidation at around 2000 °C and 40 MPa of ZrB2+20vol.%SiC nano-powders was used to minimize the oxidation and obtain fine granules with high densification. The densification of the Argon-gas purged nano-composites is higher compared to those consolidated without Argon gas purging. The EDX analysis showed a strong reduction in the oxygen peak for the Argon gas purged composites. The XRD spectra also support this observation with less ZrO2 phase composition in Argon gas purged composites. The Vickers micro-hardness showed slightly lower values for Argon gas purged composites though they have higher densification.