Effect Of Coiling Temperature On The Mechanical Properties Of Hot Rolled Multi Phase 800 Mpa Steel

The influence of the coiling temperature after hot strip rolling on the microstructure and on the tensile and hole expansion properties of a 800 MPa multiphase steel was investigated. For the temperatures between 150°C and 600°C the microstructure consisted of a ferritic matrix with a dispersion of fine martensite-austenite (MA) and regions of degenerated upper bainite. In all cases the ferrite presented a heterogeneous mixture of polygonal, quasi-polygonal and acicular grains. The yield and tensile strengths showed a tendency of decreasing with the increasing coiling temperature, probably because of the larger fraction of MA particles at lower temperatures and higher fraction of quasi-polygonal ferrite at higher temperatures. The elongation was not significantly affected by the variation of coiling temperature. The average hole expansion ratio showed a maximum of 80% for the material coiled at 400°C and fell below 50% only for the coiling temperature of 150°C, probably due to the larger hardness difference between the ferrite matrix and the MA particles.