Effect Of Compound Additives On Synthetic Magnesium Aluminate Spinel Under Low Temperature

Magnesium aluminate spinel is widely used in the metallurgical industry as refractory material, however, natural magnesium aluminate spinel is rare and most of the magnesium aluminate spinel is synthetic. The traditional synthesis of magnesium aluminate spinel often needs high temperature, which leads to more energyconsumption. In this article, solid phase sintering process was employed to synthesize magnesium aluminate spinel, in which, magnesium and aluminum oxide were used as raw materials and magnesium and aluminum powder were used as composite additives. The mass ratio of magnesium and aluminum on the effect of synthesis of magnesium aluminate spinel and the characteristic of the synthesis at different temperature and time was discussed. Experiment found that the synthesis temperature was observably lowered when the addition of magnesium and aluminum was 2.0% and 1.0% respectively.