Effect of Technological Conditions on Phosphorous Enrichment during Melting Adjusting Process of Converter Slag

"The effects of adjusting technology on the phosphorous enrichment in converter slag were investigated. The results showed that the grain size of 2CaO·SiO2 with high phosphorus containing content increased slightly with the decreasing of cooling rate, and the proper cooling rate was confirmed to be about l.0°C.min-1. Moreover, the morphology of the phosphorus-rich phase of 2CaO·SiO2-3CaO·P2O 5 was changed from granular for the higher basicity of converter slag to the coexistence of granular shape and rod-like for the lower basicity of adjusted slag. With the addition of adjusting agent such as SiO2 to lower the basicity of converter slag, the phosphorus in converter slag could be transferred into 2CaO·Si02 phase effectively, and P2O 5 content in high phosphorus containing phase reached to above 30%.IntroductionThe yield of converter slag is very large in China, but most of the slag is stacked usually after the separation of iron, which not only takes up a lot of land, but also affects the ecological environment seriously. Therefore, improving the comprehensive utilization and value-added products of converter slag is of great significance to recycle the steelmaking slag[l-3]. On the other hand, the refining of hot metal with high phosphorous content is an unavoidable problem with the decreasing of high grade iron ore, and as a result, more amounts of high phosphorus containing steelmaking slag are produced. However, the current recycle of converter slag is more focused on the emission reduction and reuse of steelmaking slag inside the iron and steelmaking process without considering the recycle of phosphorous resources[4-6]. At the same time, the development and utilization of phosphate ore as a strategic resource is drawing more and more attention, but the phosphate ore in China is mostly low grade and significant amounts of tailings are produced which is harmful to the environment. Therefore, it is important to separate phosphorous resources in steelmaking slag which can be used as phosphate ore for fertilizer material[7-9].Literature studies showed that most of the phosphorus in steelmaking slag existing as 2CaO·SiO2-3CaO·P2O 5 solid solution phase in 2CaO·SiO2 particle. The P2O 5 content in the phosphorus containing phase is very low due to the fact that the basicity of converter slag is usually high and the precipitated amounts of 2CaO·SiO2 particles during cooling are very large, resulting in the fact that the P2O 5 contents in 2CaO·SiO2-3CaO·P2O 5 solid solution phase are much lower which is impossible to be used as phosphorous resources instead of phosphate ore. Thus, the enrichment of phosphorus in steelmaking slag is need[ 10-14]."