Effect of Temperature on Equilibrium Phase Relation and Liquidus of CaO-SiO2- Al2O3-FeOx System

"Thermodynamic calculation is applied to make an investigation on the equilibrium phase relations and liquids of CaO-SiO2-Al2O3-FeOx system for different temperatures. The calculated results with FactSage6.1 show that the effect of temperature on the the equilibrium phase relations and liquidus of CaO-SiO2-Al2O3-FeOx system and its sub-systems is appreciable. The liquid phase regions enlarge with increasing temperature from 1573K to 1873K, while the primary phase fields reduce distinctly.IntroductionThe main oxide components of vitrified bottom ash slag are CaO, Al2O3, SiO2, Fe2O3, MgO, and Na2O, accounting for more than 90% of the bottom ash by weight[1]. During slag processing, the knowledge of thermodynamic properties and liquidus temperature in the related slag systems is highly required [2, 3], which is not yet available. Through literature survey [4-6], it is clear that the systematic information on the concerned complex slag system is scarce. So far the engineers in the field have to make assumptions of the thermodynamic properties of the simplified oxide system, without taking into consideration the interactions of the different oxide components, which hinders the development of the slag valorization and utilization. In order to provide thermodynamic properties for the application of the vitrified bottom ash, the six-component oxide system (CaO-MgO-Al2O3-SiO2-FeOx-Na2O) is highly required. A preliminary phase diagram of the CaO-MgO-Al2O3-SiO2-FeOx-Na2O system can be obtained from extrapolation of the thermodynamic functions of constituent subsystems such as CaO-SiO2-FeOx-MgO, CaO-SiO2-FeOx-Al2O3, CaO-SiO2-Na2O-MgO and CaO-SiO2-Na2O-Al2O3. In this work, the equilibrium phase relation and liquidus of CaO-SiO2-FeOx-Al2O3 system, one subsystem of the concerned complex slag system, are calculated and the effect of temperature is also discussed."