Effects of Solute Mg Concentration on Mechanical Properties and Dislocation Characteristics of Al-Mg Alloy

"In general, there is a strong correlation between dislocation characteristics and mechanical properties of aluminum alloys. In this study, dislocation characteristics of tensile deformed Al-Mg alloys were examined by transmission electron microscopy. An Increase in the solute concentration, ranging between 0.3 and 1.1%, Mg leads to increase in strength and decrease in uniform elongation. The accumulation of dislocations during the tensile deformation is observed in lower strain as the concentration of solute Mg in the alloy is higher. It is believed that the solute Mg in Al-Mg alloy promotes the accumulation of dislocation during the tensile deformation resulting in the decrease in elongation.INTRODUCTION The influences of the amount of Mg concentration on the tensile properties of Al-Mg alloys has been investigated by many researchers. It has been understood that the tensile ductility of Al-Mg alloy is higher for the Al-Mg alloys with higher Mg concentration beyond 2 mass% (Mukai, Higashi, Hirano & Tanimura, 1993). Uchida and Yoshida (1995) reported the formation of microbands during the tensile deformation due to the localization of dislocations, and the amount of microbands were reduced when the Mg concentration of the Al-Mg alloy was increased from 3 to 9 mass%. Their study suggested that the dynamic recovery of dislocation was retarded due to the increase of the Mg concentration during the tensile deformation, which resulted the increase in ductility. On the other hand, in the case of Al-Mg alloys with the Mg concentration less than 3 mass%, the reason why the ductility of Al-Mg alloys decreases with increasing Mg concentration has not been sufficiently investigated. In general, the Mg concentration used for automotive usage is less than 1 mass%, in the case of Al-Mg-Si alloys (Aoki, 2013). Therefore, to clarify the roles of Mg in the low concentration range on ductility of aluminum alloys and to elucidate its mechanism contribute to alloy design of Al-Mg-Si alloys having good formability."