Elevated Temperature Deformation Behaviors And Microstructure Evolutions Of Cast Sa508-4n Steel

The deformation behaviors under both tensile and compressive forces and microstructure evolutions of cast SA508-4N steel were investigated at elevated temperatures. True stress-strain data were obtained from hot deformation experiments performed on a Gleeble-3500 thermal-simulator under different temperatures (750-1200C) and strain rates (0.001-10 s-1). The reduction of area decreases as a function of temperature from 750C to 900C and then increases. At 1200C, the reduction of area reaches more than 99% with the strain rates of 0.5 s-1 and 1.0 s-1. The dynamic recrystallization under compressive stress occurs at 800C under low strain rate and a complete dynamic recrystallization can be observed when the temperature reaches above 1100C. A “two-stage” flow stress constitutive model concerned with dynamic recovery and dynamic recrystallization was established based on the true stress-strain data. This model shows good agreement with experiment results. Moreover, we developed a dynamic recrystallized grain size model to describe the average grain size after complete dynamic recrystallization.