Extracting AliO3 from Coal Gangue by Carbonthermal Reduction – Alkaline Leaching Process

"Coal gangue is industrial waste containing Al2O3 and SiO2 with great recycling and reuse values. This work is aimed at extracting Al2O3 content in the coal gangue by a process of carbonthermal reduction - alkaline leaching. The Al2O3 and SiO2 contents first became a mixture of SiC and Al2O3 in the process of carbonthermal reduction, and then Al2O3 was separated by leaching in NaOH solution, thus producing the sodium aluminate solution for Al(OH)3 precipitation. The products generated at various stages in the process were inspected using XRD and chemical analysis. The effects of parameters such as reduction temperature, carbon ratio, NaOH concentration, leaching time, leaching temperature, stirring speed, etc were investigated in details.IntroductionCoal gangue is an industrial residue resulted from the process of coal mining and washing, accounting for 100 - 150 kg with 1 ton raw coal mined. The existence of coal gangue in large quantities has become a serious problem for environment pollution. On the other hand, the chemical compositions of coal gangue are Si02 and Ah03 primarily. In China, the accumulation storage capacity of Ah03 in coal gangue is not less than 600 million ton at a rough estimate, which should be considered as an abundant second resource [1]. If the alumina can be recycling and reused effectively from coal gangue, it will not only reduce the imperilments caused by coal gangue, but also yield good economic returns.Generally, the processes of extracting Al2O3 from coal gangue can be divided into acid leaching (vitriol or hydrochloric acid) and alkaline leaching (mostly NaOH) [2]. The acid leaching processes have many problems, such as lower leaching ratio, corroding the equipments, recycling the spent acid hardly, etc. The primary matter of alkaline leaching process is silica dissolving with alumina, which brings perplexing desilication process, alumina loss seriously and higher energy consumption."