Fabrication Of BaNd2Ti4O12/Bi4Ti3O12/BaNd2Ti4O12 Laminated Ceramics By Spark Plasma Sintering

Laminated ceramics have received widely scientific and commercial attention because their properties, such as mechanical properties and electrical properties, can be tailored by adjusting the structure, thickness and composition of the different layers. For example, ferroelectric Bi4Ti3O12 (BIT) which has a positive temperature coefficient of dielectric constant (,E) can be used to modify the negative tE of typical microwave dielectric ceramic BaNd2Ti4O12(BNT), However, BaNd2Ti4O12/Bi4TiO12/Bi4Ti3O12/BaNd2Ti4O12 (BNT/BIT/BNT) laminated ceramics could not be prepared by the general method because the optimal sintering temperature of BaNd2Ti4O12 ceramic (around 1350°C) was much higher than that of Bi4Ti3O12 ceramic (around 1100°C). In this research, a new method of spark plasma sintering (SPS) combined with post-sintering was successfully proposed to prepare BNT/BIT/BNT laminated ceramics. It was divided into three steps. In first step, the BaNd2Ti4O12 ceramics were prepared by conventional sintering method. In second step, the calcined and pre-pressed Bi4Ti3O12 powders were sandwiched between BaNd2Ti4O12 ceramic pellets and spark plasma sintered at 900°C for 10min to synthesize BNT/BIT/BNT composite ceramics. In the last step, a post-sintering was employed to reoxidize the partially reduced BNT/BIT/BNT composite ceramics. The results of scanning electron microscopy (SEM) and electron probe microanalysis (EPMA) showed that BNT layer and BIT layer were well bonded and no significant interfacial infiltration between them was observed. The sandwiched BNT/BIT/BNT ceramic with 10.7% BIT in volume has a dielectric constant of 92.85, a low dielectric loss of 01068 and a small temperature coefficient of dielectric constant of 35 ppm/°C at MHz.