Fabrication of Replicated Open-Cell Aluminium Foams Using Recycled ADC12 Aluminium Alloy

"Recycling of ADC12 alloy scraps for fabrication of open-cell aluminium foams has been conducted via pressure infiltration method of replication process. The scrap, up to 50 wt.%, was melted with pure aluminium billet, followed by infiltration in a replicated mold of polyethylene foam structure. Compared with the pure aluminium foam, the compressive strength and hardness are higher for the foams with recycled scraps. The increase in foam mechanical properties is due to the presence of Si hard phase in Al matrix. The strength and hardness of the foams also increase with increasing contents of the scraps.IntroductionRecently, open-cell metallic foams have been brought to considerable attention of many industries due to their superior properties; such as large surface area, high specific strength, thermal conductivity, high service temperature and excellent anti-microbial activity, that cannot be found in conventional materials [1, 2]. Typically, open-cell foams are used in functional applications for which a requirement of high strength materials is not demanded. Good examples of such applications include heat exchangers, bone-replacement implants, interconnects, catalyst supports, and sound insulators.Among all types of open-cell metallic foams, aluminium (Al) is the most widely used base metal, due to low material cost, low density, low melting temperature and good corrosion resistance. To improve mechanical properties of Al foam, modification of foam microstructure with addition of alloy elements or ceramic particles is commonly carried out [3, 4]. ADC12 alloy is a typical die-casting Al alloy with high content of silicon (Si) close to the eutectic point in Al-Si binary phase diagram. The alloy is extensively used in the casting industry, due to high wear and corrosion resistance, low coefficient of thermal expansion and excellent castability [5]. The mechanical properties of Al-Si alloy are strongly dependent of Si content."