Formation of Ti(C,N) in Blast Furnace Slag Bearing High TiO2

"The flow properties of the blast furnace slag bearing high TiO2 at high temperature like the viscocity may change a lot due to the formation of the carbonitride inside, causing serious problems on the separation between the metal and the slag. Therefore, the critical condition of the formation of Ti(C,N) in blast furnace is vital importance for the ironmaking process with iron ore bearing titania. In this study, the formation of Ti(C,N) in blast furnace and the influences of various factors on the Ti(C,N) formation are investigated by FactSage. It is found that the mass of Ti(C,N) would reach the maximum at 1480 oC, and the product is mainly TiN below 1620 oC, while it is mainly TiC above 1620oC. The order of the factors by the importance from strong to weak was: temperature, the content of TiO2 in slag, basicity of slag, the content of MgO and Al2O3.IntroductionThe titanium dioxide (TiO2) in iron ore bearing titania will be partly reduced by carbon to titanium carbonitride (Ti(C,N)) in blast furnace, causing serious problems on the separation between the metal and the slag because of the change of flow property. Therefore, the critical condition of the formation of Ti(C,N) in blast furnace is vital importance for the ironmaking process, especially for the smelting of iron ore bearing titania. Extensive experimental data in regard to the formation of Ti(C,N) has been reported in numerous papers[1-6]. However, only some discrete data can be obtained by experiment, and it is difficult to detect the mass of Ti(C,N) in slag. In addition, the experiment is difficult to be proceeded when the temperature is above 1600oC. Therefore, it is very difficult to make clear the critical condition of the formation of Ti(C,N) by experiment."