Function of High Pressure Roll Grinding in Production of Magnetite Oxidized Pellets

"Function of High Pressure Roll Grinding (HPRG) in production of oxidized pellets from magnetite concentrate as raw material was systematically studied. It was found that bentonite dosage decreased from 1.3% to 0.8% if specific surface area of magnetite concentrate pretreated by HPRG was up to 2553.41cm2.g-1. The green ball quality improved obviously due to the increase of specific surface area and fine particles content, and the improvements of size distribution and the ballability of pretreated materials. However, the decrease of pellet porosity accelerated the primary solid phase reaction and oxidation reaction, which made the pellets surface form compacted layer that handicapped the diffusion and migration of oxygen, promoting the formation of double layer structure of finished pellet. Consequently, the compression strength of preheated and roasted pellets was not markedly improved by HPRG.IntroductionWith the increase of proportion of pellets in the BF recently, the technical-economic index of BF has obviously been improved. Consequently, the production and the quality of BF pellet are given more attention [1]. However, with the decrease of the quality of iron ore concentrate, the problems such as poor ballability, high bentonite dosage, high preheating and roasting temperature are becoming the great challenges to not only the quality of finished pellets, but also the energy consumption [2, 3]. In order to overcome these problems, mechanical pretreating technologies such as the High Pressure Roll Grinding (HPRG) and Damp-grinding are widely applied. HPRG has a number of advantages such as low energy consumption, high productivity and easy-maintaining. It is more economic and environmentally friendly than the Damp-grinding technology [4, 5]. A great number of experiments have revealed that HPRG can improve the quality of hematite pellets. Although there are some studies of function of HPRG in the magnetite oxidized pellet production, they are not comprehensive and systematic, especially to the preheating and roasting system [1, 2, 6, 7]. Accordingly, the influence of HPRG on the pelletizing system and the preheating and roasting system are systematically studied in production of magnetite oxidized pellets in this article."