High Temperature Experimental Investigations and Thermodynamic Modelling in the FeTiO3-TiO2 Ternary Slag System

"The current work presents new experimental data in the iron-unsaturated region of the FeTiO3-Ti2O3-TiO2 slag system. The samples are prepared by melting pure reactants in a high frequency induction furnace that employs a cold crucible. A similar experimental set-up has been described in literature and proven suitable to investigate high titania slags. The FeO content of the samples range from 3.7 to 21.8 wt% and the Ti2O3 content range from 3.6 to 30.1 wt%. The liquidus temperatures of the samples are measured in-situ by a spectropyrometer and range from 1450 to 1645 °C.In addition, an improved thermodynamic database for the FeO-Ti2O3-TiO2 system has been developed. Ternary parameters have been included and optimized to fit previously published experimental data. This optimization minimizes the discrepancy between experimental data and thermodynamic calculations as previously discussed in literature. New liquidus projection plots are proposed for the FeO-Ti2O3-TiO2 and the FeTiO3-Ti2O3-TiO2 systems.IntroductionIlmenite (FeTiOs) smelting is a relatively small industry world-wide. However, a reasonable focus on the process has been applied in Norway due to the location of one such smelter in Tyssedal, which is located in the western part of Norway. The process is essentially carbothermal reduction, where most of the iron in the ilmenite is reduced to its metallic state, and the titanium oxide is concentrated in the slag product. The metallic iron is sold as a high purity pig iron and finds applications in cast products. The slag concentrate is further processed for the production of TiOvpigment and/or titanium metal. This further processing can be performed through different routes according to the purity of the slag concentrate."