High Temperature Interactions between Si3N4 and Tic

Kinetics and mechanism of the chemical interactions between Si3N4 and TiC were investigated by isothermally reacting samples under nitrogen and argon atmospheres at temperatures between 1600°C and 1700°C? The initial composition of the powder compact contained 20, 30 and 40 volume per cent TiC? Kinetic analysis were performed by measuring mass losses and composition of the titanium carbonitride (TiC1-xNx) at predetermined time intervals? It was found that in the Si3N4-TiC system the degree and rate of the reactions increased with increasing temperature and content of TiC in both nitrogen and argon atmospheres? Si3N4 in the presence of TiC was stable in nitrogen atmosphere and the reactions were confined to Si3N4/TiC and TiC/N2 interfaces? At both interfaces interchange reaction occurs by simultaneous diffusion of nitrogen towards the centre of the particle and desoprtion of carbon in the opposite direction resulting in formation of titanium carbonitrides with various compositions? Reaction products under nitrogen atmosphere were B-SiC, TiCl1-xNx and N2? The maximum "x" value in TiC1-xNx was found to be 0?67 under nitrogen atmosphere? Si3N4 was found to be unstable in argon atmosphere in the presence of TiC and dissociated into liquid silicon and nitrogen gas within approximately four hours of reaction time, depending on temperature? The reaction mechanism in the initial stages of the interaction between Si3N4 and TiC under argon atmosphere proceeds similar to reactions under nitrogen atmosphere? However, considerable amount of Si3N4 dissociates within the first half hour? Liquid silicon aggressively attack both TiC1-xNx and unreacted or partially reacted TiC particles through cracks and pores and diffuses into interier part of the particle forming liquid solutions? After this stage, reactions under argon atmosphere proceeded according to Si-Ti-C ternary system?