Hot-Pressing And Mechanical Properties Of Bn Based Composites

BN (Boron Nitride) based composites were prepared with hot-pressing by using h-BN as main material in ceramic preparation process. The relative density, bending strength, vickers’ hardness, thermal shock resistance, thermal expansion coefficient, thermal conductivity, phase composition and microstructure were tested and analyzed by using modern testing technology. The results indicate that the best formula is B, the relative density is 97%, the bending strength is 260 MPa, the hardness is HV5 343kg/mm2, the thermal expansion coefficient is 2.8×10-6℃-1, the thermal conductivity is 22 W/(m.K) and have no crack after thermal shock for 20 times by water cool. XRD analysis indicates that the main phase compositions are h-BN, β-Si3N4 and sialon. SEM studies show that the grains wrapped up by solid solution.