Indium Extraction Process from Sulfuric Pressure Leaching Solution for Vacuum Furnace Germanium Slag

"The enrichment and separation of scattered metal indium component in the pressure leaching solution with sulfuric acid from vacuum furnace germanium slag were studied by iron substitute and P204 extraction, which is supplied by shaoguan smelter. The experimental results show that the extracting power of P204 for indium from pressure leach solution is powerful. The optimal technological condition were the ratio of P204 and sulphonating serosene 3:7, phase ratio 1:3, solution pH 1.2, and extracting 5 minute. The enrichment indium solution of 21.7 g/L In at 95.2% recovery ratio was obtained by three-stage counter flow extraction and four- stage counter flow stripping.IntroductionScattered metals, such as Indium and germanium, were inriched as intermediate product or by-product during the metallurgy process of other non-ferrous metals, such as lead, zinc, copper and tin. For example, the indium and germanium were inriched in vacuum furnace germanium slag, which is the by-product of zinc vacuum distillation operation from hard zinc. It is difficult to recovery the indium from the vacuum furnace germanium slag, because the indium content is low, and the chemical composition and phase compositon were complex.Recovery indium from bearing indium zinc slag was researched extensively, such as pressure acid leaching, high temperature evaporation, solvent extraction method[l-7], acid leaching method has the advantages of high leaching rate, which can be separated hydrochloric acid, sulfuric acid and silicon fluoride acid systems. Solvent extraction method has the advantages of low production cost, fast reaction speed, high enrichment ratio, and simple operation."