Influence of Crystallization Conditions on the Preparation of Mesoporous Materials from Natural Zeolite

"Mesoporous materials with large specific surface area, pore size, and pore volume have been widely used in many fields such as ion exchange, gas separation, adsorption, and catalysis. Mesoporous materials prepared using natural zeolite have the advantages of both acid and alkali resistance. In this work, mesoporous materials were prepared using natural zeolite as the starting material and diethylenetriamine (DETA) as a template. The resulting samples were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD) and N2 adsorption-desorption experiments. The influence of the crystallization temperature and crystallization time on the specific surface area, pore volume, pore size, and morphology of the resulting mesoporous materials are also discussed. Our results show that for an increase in both the crystallization temperature and time, the average pore size first increases then decreases, while the specific surface area first decreases then increases. Based on this work, we concluded that the optimal crystallization temperature was 2003 and the optimal crystallization time was 60 h. These conditions gave an average pore size of 17.93 nm, a pore volume of 0.048 cm3g-1, and a specific surface area of 16.48 m2g-1.INTRODUCTIONMesoporous zeolite, as the name implies, is a highly porous crystalline zeolite. This material is of interest due to its high hydrothermal stability, its adsorption and diffusion properties for macromolecules, and its excellent selectivity and activity as a catalyst. In recent years, it has become a hot spot among research of porous catalytic materials and has been widely used in petroleum and natural gas processing, fine chemical processing, various adsorption and separation tasks, and other uses (Carvalho & Urquieta- Gonzalez, 2015; Teh, Triwahyono, Jalil, Mukti, Aziz, & Shishido, 2015)."