Investigations On The Role Of Copper In Causing And Nickel In Preventing The “hot Shortness” In Steels

An extensive investigation into the role of low copper contents on the hot ductility of C-Mn-Al steels has been carried out in order to better understanding the problem of “hot shortness”. Previous work has suggested that this problem results from the build up of Cu that occurs at the surface of the steel as a consequence of the preferential oxidation of iron. This causes the formation of a Cu-rich film of low melting point. A nickel addition has been reported as a solution to the problem, since it increases the solubility of copper in the austenite. After hot tensile testing to failure, samples of Cu-containing steels have been examined using optical, scanning and transmission electron microscopes. Recently published results indicate that copper, in addition to precipitating out as CuS, also segregates to MnS inclusions forming a shell around them. This does not seem to impair the hot ductility under an inert atmosphere, but may have serious consequences under an oxidising environment and lead to “hot shortness”. The influence of nickel in improving the hot ductility seems to be due to it forming a higher melting point alloy with the segregated copper. Data from this incomplete work also suggests that Ni reduces the precipitation of CuS particles. Current investigation carried out using confocal microscopy still to be completed will improve the understanding of the role of copper and nickel on the problem of “hot shortness”.