Isothermal Bainite Transformation of Cr5 Steel under Pulsed Current and Pulsed Magnetic Field Treatment

"Pulsed current and pulsed magnetic field have been applied to the bainite transformation of Cr5 steel. Three groups of experiments were conducted. In the first group, ordinary resistance furnace was used for heat treatment. The Cr5 specimens were rapidly heated up to austenitization temperature 940 °C, held for 20 min, air cooled to bainite transformation temperature 350 °C, held for 10, 20, or 40 min and then air cooled to room temperature. The second and the third group shared the same temperature-time curve with that of the first group, but their heat resources came from the Joule heat produced by pulsed current. 1.5 T pulsed magnetic field was exerted on the third group specimens when they were held at 350 °C, but the second group specimens did not undergo the treatment of magnetic field. It was found that both pulsed current and pulsed magnetic field obviously retarded the bainite transformation. The phenomena were discussed in terms ofliterature results.IntroductionApplying pulsed current and pulsed magnetic field technology are very pronnsmg ways to change the microstructure of materials by affecting the phase transformation process. People had found that pulsed current dramatically influences the behaviors of materials, for example, electromigration effect [l], the solidification of metals and alloys [2, 3], electroplasticity [4, 5], crystallization of amorphous alloys [6], healing of metal materials [7] and so on. As to pulsed magnetic field technology, a lot of effort had been spent on grain refinement in solidification of metals [8, 9], recrystallization of cold-worked metals and alloys [10] and Fe-based alloys solid-state phase transformation [11, 12]. Though application of pulsed current and pulsed magnetic field technology have proliferated in recent years, investigation on their effects on solid/solid phase transformation, especially bainite transformation, is lacking. The aim of this paper is to show the effects of pulsed current treatment (C-T) and the combined treatment of pulsed current and pulsed magnetic field (CM-T) on bainite transformation of commercial Cr5 steel"