Leaching of Gold from Waste Printed Circuit Boards in an Iodine-Iodide Solution and Regeneration of the Spent Lixiviant

The objectives of this study were to propose a viable alternative method for recovery of precious metals such as gold (Au), silver (Ag) and palladium (Pd) from waste printed circuit boards (WPCBs) and to regenerate the spent lixiviant solution for reuse. The proposed method generally consists of several steps as follows: 1). iodine-iodide leaching for metals extraction; 2). separation and recovery of precious metals and metal impurities from a pregnant leach solution; 3). regeneration of the spent iodine-iodide solution/lixiviant. In this method, more than 99% of Au leaching was achieved in the iodine-iodide solution from the solid residue of WPCBs that was obtained via sequential processes including incineration at 800 ?C and high pressure oxidative leaching with a diluted sulfuric acid at 120 ?C, while the leaching of Ag and Pd was less than 1%, respectively. Besides Ca, Cu, Ni, Co and Zn as main metal impurities, leaching efficiency of other metals did not exceed 1%. The precious metals and base metals as metal impurities present in the pregnant leach solution were separated and recovered by precipitation using L-AA and NaOH solutions. About 99.8% Au, 81.7% Ag and 72.8% Pd were recovered from the pregnant solution at pH of 2 with the addition of 0.1 M L-AA as precipitating agent. The remained small amounts of precious metals and metal impurities were precipitated at pH 13 using 1 M NaOH. The spent lixiviant after sequential precipitation was regenerated in the presence of hydrogen peroxide, hydrochloric acid and potassium iodide. It was revealed that over 90% of gold could be extracted from the residue of WPCBs with the regenerated lixiviant solution.