Manganese Oxide Composites as Electrode Material for Electrochemical Capacitors

The Pseudo capacitance of layered type Mn02 electrode material for electrochemical capacitors (EC's) was investigated. MnO2 was synthesized in our laboratory. Mn02 was prepared from heating of KMn04 at 300°C in air. Cyclic Voltammetry (CV) experiments were carried out using three electrode system, Saturated calomel electrode as reference electrode, platinum mesh as a counter electrode, and MnOz composite material mounted in a platinum mesh used as a working electrode. Two kinds of composite working electrode materials were used, one was mixture of MnOz and 25 wt% acetylene black, while the other was MnOz, 25 wt% acetylene black and 25 wt% carbon. All the experiments were carried out at 25OC. A maximum specific capacitance of 130 Fig and 118 Fig were observed at the scan rate of 2 mV/s and 20 mV/s respectively in 1M KC1 for composite electrode made with carbon. Results obtained in this study are compared with that of other electrode materials.