Mechanically Activating Soda Leaching Of Low-Grade Tungsten Ore

Leaching of Shizhuyuan low-grade refractory tungsten ore was carried out in a mechanically activating reactor. The effect of experimental parameters-temperature, amount of Na2C03, addition of NaOH, ratio of liquid to solid and leaching time - on the recovery of WO3 was studied. The WO3 recovery up to 96.99% have been achieved when the tungsten ore was digested by soda not more than three times the stoichiometric amount at 185-195°C for 1 .O-2.0 hours. Iso-extraction countour diagrams were drawn to illustrate the effect of various parameters on leaching. The WO3 recovery could be expected to increase 10-15% compared to that of conventional soda autoclave process.