Micro Wave Reflection Loss of Ferric Oxide

"The microwave reflection loss (RL) of ferric oxide is studied in the temperature range from 297 to approximately 1400 Kat frequencies of 915 and 2450 MHz. It is shown that the maximum microwave absorption with RL of -38.46 and -35.97 dB can be obtained for ferric oxide having thicknesses of 0.03 and 0.01 m at 915 and 2450 MHz, respectively. The maximum absorption peak with RL below -10 dB is in a 250 K temperature range from 723 to 973 Kat 915 MHz, which shifts to the range between 823 and 1073 K at 2450 MHz. This migration is in good agreement with the variation of the dielectric loss tangent of ferric oxide.IntroductionMicrowave irradiation has distinguishing characteristics such as volumetric and selective heating compared with conventional methods, leading to extremely broad applications in materials heating and processing [1-5].The efficiency of microwave heating was found to be dependent on various factors, such as microwave power [6], frequency [7,8], radiation time [8], applicator geometry [8], sample microwave absorption properties and position as well as dimension [9-11 ], etc. Among these parameters, sample dimension plays an important role but is usually neglected by researchers in microwave processing of materials. In fact, although numerous studies have been directed toward the utilization of microwave energy to assist materials heating and processing, few reports were released on the effect of sample dimension [12,13].This is because all aforementioned factors influencing microwave heating generally exert interactive effects to each other during the heating process, making clarification of the effect of sample dimension difficult. Therefore, it is necessary to propose a parameter or concept for quantifying the effect of absorber dimension on microwave heating, increasing heating efficiency."