Microstructural Characterization of Nanomaterials Produced From Co-Products of The Ethanol Production (DDGS)

"Reduction of combustion-emitted greenhouse gases, which are associated with global warming, may be achieved by use of CO2-neutral alternative fuels, such as bio-ethanol. Distillers Dried Grains with Solubles (DDGS) are the main co-products of the com-grain-based ethanol industries. In 2009, the North American production of ethanol from com was about 38 billion liters, which generated approximately 31.5 million tons of DDGS. Samples of DDGS were pyrolysed at temperatures of 600-1000 °C in a two-stage laminar-flow horizontal furnace, and a catalyst system was used to synthesize nanomaterials. This work presents a microstructural characterization of these nanomaterials by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Results showed that the nanomaterials produced from pyrolysis of DDGS were in the form of long, entangled, rope-like structures with rugged walls, lengths in the tens of microns, and axially non-uniform diameters in the range of 100-300 nm.IntroductionThe interest in ethanol has increased considerably worldwide due to the necessity of finding renewable and cleaner energy resources [1, 2]. According to the Renewable Fuels Association (RF A), the world ethanol production in 2008 was approximately 65.7 billion liters (17.3 billion gallons), which figure represented a 24% increase in the production over that in the previous year [3]. The major producers of ethanol are the USA and Brazil, which together account for 90% of world production. The main feedstock for ethanol in USA is com grain, whereas sugarcane predominates in Brazil [2-4]."