Microwave Thermal Prereduction With Carbon And Leaching Of Chromite Ore Fines

The ferrous removal process after carbothermic reduction of chromite fines with microwave heating combined with leaching was investigated. Under the following conditions: Reaction temperature: 1150 , Reaction time : 40min, Semi coke ratio: 12% , the iron content of the reduction product : 13.05% . Metallization achieved was 52.7%. Reduced chromite was leached with 8% of H2SO4 and FeCl3 aqueous solution. The results show that: the recovery rate of chromium can reach 88.06%, the mass ratio of chromium to iron is 3.5:1 for leaching 30 minutes with 8% of H2SO4; the recovery rate of chromium can reach 88.91%, the mass ratio of chromium and iron is 2.56:1 for leaching 4h at room temperature with FeCl3 aqueous solution (100g/L). The leaching time of latter is longer but can realize the circulation effectively and reduce the waste liquid processing problem.1