Nickel Recovery from the Alloy Al2Ni and the Mixtures Al-Ni, Al2O3-Ni and Al2O3-NiO. Comparative Study by Direct Chlorination of the Species.

"The separation of nickel from the aluminum present in spent catalysts and different metallic industrial residues, is proposed in the following systems: alloy Al2Ni and the mixtures 50 wt% Ni + 50 wt% Al, 10 wt% Ni + 90 wt% Al2O3 and 12 wt% NiO + 88 wt% Al2O3. The experiments were carried out in a tubular reactor with a flow of 2 l/h of gaseous chlorine and from 200 ° to 800 °C. The final products of the reaction, extracted from the hottest zones of the reactor where characterized by XRD, SEM, EDS, AA and XRF, as NiCl2 y NiCl2.6H2O while in the coldest regions AlCl3 was deposited in the first two cases and in the other there was a residue of ?, a- Al2O3, sometimes mixed with some remainder of Ni and NiO. The procedure attained different separation factors which showed the optimun conditions for the recovery of both metals. Introduction Some studies of nickel corrosion were carried out in chlorine gas at temperatures above 950ºC, and suggested that nickel is not corroded below 538ºC. [1] However, in a previous work it was shown that the chlorination allows the separation of nickel from aluminum and the formation of NiCl2 was detected from 200ºC in binary mixtures Ni-Al 50 wt%, for isothermal conditions in chlorine flux. [2] Other researchers obtained selective chlorination above 650ºC of a fly ash containing 1.4 wt% of Ni and other metals (V, Mg, Al and Fe). The Ni was separated from the Mg and NiCl2 started to vaporize at 550ºC and was after condensed in a zone of the reactor above 380ºC with 90% of purity. [3]"