Numeric Simulation of the Cooling Process of the Iron Ore Sinter

"The iron ore sinter is one of the main raw materials for the blast furnace (BF) process. In the production of iron ore sinter, the cooling speed of the sinter determines its quality. In addition, the heat recovery devices are installed in the cooling machine for energy saving. The cooling parameters like gas flow rate and the size of sinter should be optimized for getting the gas with a higher temperature and a good quality of sinter simultaneously. In this study, the commercial simulation software COMSOL was used to establish a model for simulating the cooling process of the iron ore sinter. Moreover, three different gas flow rate (1.5, 3, 5m/s) and three different diameter of sintered particles (50, 70, 100mm) were investigated with the model. As a result, in certain porosity, a higher cooling speed was achieved when smaller size or larger gas flow rate was used. And lower gas flow rate was beneficial for the heat recovery. The model could intuitively present the exchange of heat between the sinters and air, as well as the flow and temperature fields during the cooling process.IntroductionIron ore sinter plays a great role in iron and steel industry for many Asian countries such as China, Japan and India. As a part of the sintering procedure, the impact of cooling process on the quality of iron ore sinter couldn't be neglected. On the other hand, the massive iron ore sinters which were at high temperature contain extremely large amount of heat. However, it was reported that there's very few of them recovered in China with an average recovery rate of nearly 10.5% at 2004 [1]. Thus, more reasonable cooling procedure should be developed to get high quality product and heat recovery rate simultaneously."