Optimization of Effective Parameters in Gold Extraction Process from Poly Metal Ore, Using Thiourea as a Cyanide Alternative and Sodium Cyanide (641bd78f-36ca-4ae1-92b5-a21b7d22407e)

Due to detrimental effects of cyanidation process on the environment in gold industry, application of cyanide alternatives such as thiourea are being highly considered in recent projects. In this study, the extraction of gold from poly metal ore, using thiourea was precisely investigated. The representative sample contained 2.5 ppm Au and 160 ppm Ag. The sample was categorized as oxide gold ore, because the main part of its pyrite was changed to iron oxide and hydroxide such as goethite and lepidocrosite. According to mineralogy, the main gangue mineral was quartz. It shows that gold grains are free and interlocked with quartz matrix. Also, the presence of a high amount of silver in free and sulfide forms and also the low content of other sulfide minerals such as base metal sulfides is a remarkable point of these studies. In the gold extraction process with thiourea, there are several parameters that affect the rate of gold dissolution such as concentrations of thiourea as a gold lixiviant and ferric sulfate as an oxidant, pH and size fraction of feed and leaching time. The influence of these parameters on the gold dissolution rate were investigated and optimized. The results showed that the concentration of thiourea is the most influential parameter which could increase the gold recovery to 71% (at 10 g/kg sample). The optimal amount of ferric sulfate was determined as 6 g/kg sample. Also, the optimal levels of size fraction of feed and pH of solution were 88% under 75 micron and 2 as acidity; respectively. Leaching time was 6 hrs. In addition, this sample was leached with cyanide and the optimized values of size fraction of d88=75 microns, pH=10.45, 2500 ppm of sodium cyanide with time leaching of 24 hours were concluded for maximum recovery of gold in solution. Finally, the results of cyanidation tests were compared to the thiourea dissolution after optimizing all affected parameters in cyanidation process.