Part I – January 1969 - Papers - An Investigation of the Yield Strength of a Dispersion-Hardened W-3.8 vol pct Tho2 Alloy

The yield strength of a dispersion-hardened W-3.8 vol pct Tho,alloy, in both the recovered and recrys-tallized condition, was investigated and cornpared with that ofrecrystallized pure tungsten over the temperature range of 325" to 2400°C. It is deduced that the Orowan mechanism is obeyed in the recrystallized alloy. In the recovered alloy, a further enhancement of the yield strength results from the retained substructure which is stable up to temperatures in excess of 2700°C. Temperature and strain rate cycling tests were also performed, and the apparent activation energy for the deformation process was derived. This activation energy, - 3 ev, for the recovered and also the recrystallized alloy was about the same as that for re crystallized pure tungsten. However, the activation volume of the recovered alloy, -10-2 cu cm, was about an order of magnitude lower than that of the recrystallized alloy or pure tungsten. This fact accounts for an enhancement oj- the temperature dependence of the yield stress of the recovered alloy. A dislocation velocity exponent of about 4 to 13 was deduced frorn the strain rate cycling tests , which is in good agreement with values reported for tungsten single crystals. VARIOUS theories have been developed to explain the enhanced yield strength of a metal containing a dispersed second phase of small hard particles. These theories are thoroughly reviewed by Kelly and Nicholson.' The theoretical models can be separated into two types. The first type assumes direct interactions between moving dislocations and dispersoids. One of the most widely investigated models for this mechanism is the bowing out of dislocations between the dis-persoids and their subsequent pinching off in order to bypass the obstacles. This is the well-known Orowan mechanism.' The second type is an indirect effect of the dispersion because of its ability to stabilize to high temperatures the substructure introduced by cold working. In this instance, the increment in the yield strength is expected to be inversely proportional to the square root of the subgrain diameter. In the present work, a quantitative study was made of the strengthening effect caused by a thoria dispersion in a recrystallized W-3.8 vol pct Thoz alloy over the temperature range 325" to 2400°C. The results are compared with the increment predicted for the Orowan mechanism based on the calculations by ~shb~.~ In addition, the alloy was tested in the recovered state so that any additional strengthening resulting from the substructure produced during fabrication could be measured. The respective contributions can be separated in this manner, provided that the particle size distribution of the dispersion remains the same in both the work-hardened and the recrystallized state. Particle size distribution measurements showed that this condition was met in the present work. I) EXPERIMENTAL PROCEDURES A) Material Production and Fabrication. The alloy investigated is essentially the same as that reported much earlier by ~effries,~ who also found the strength of tungsten to be improved by the thoria dispersion. The procedure for producing the alloy consisted of mechanically blending a thorium nitrate solution in proper concentration with tungsten oxide (WO3) powder, followed by hydrogen reduction to metal powder. After reduction, the dispersed second phase is present as thoria (Thoz). The pure tungsten powder used for comparison was produced in the same manner except that the thoria doping step was omitted. The powders were consolidated by cold pressing and self-resistance sintering in hydrogen. The resulting ingot had a cross section about 0.6 sq in. and a density about 93 pct of theoretical. The ingot was swaged to 0.174-in.-diam rod at temperatures varying from 1650°C initially to -1200°C near final rod sizes. Two intermediate recrystallization anneals were employed during fabrication. Analysis of the swaged rods is reported in Table I. B) Electron Microscopy Techniques. Carbon extraction rrPxcas prepared by a technique reported by ~00' were used to quantitatively evaluate the thoria particle size and distribution. Electron nlicrographs of extraction replicas were taken at 20,000 times but were then enlarged two to three times in printing. The areas photographed were randomly selected. A Zeiss Particle Size Analyzer (Model TGZ3) was used to count and measure the sizes of all particles present on the print. About three thousand particles were counted in determining a distribution curve. Electron transmission microscopy was used to determine the effect of annealing on the substructures of the materials. Thin foils were produced by a two-stage thinning process. The rods were first ground on emery paper to ribbons about 10 mils thick and then a jet of 5 pct KOH was used to electrolytically reduce a portion of the cross section of the ribbon. Final perforation was achieved by immersing the specimen in a 5 pct KOH solution and electrolytically polishing at a current density of about 0.3 amp cm-'. The foils were examined with a Hitachi HU-11A electron microscope. C) Tensile Testing. Tensile testing was performed in an Instron Testing Machine equipped with a radiation-type vacuum furnace which operates at about 1O"S torr at temperatures as high as 2400 °C. The same furnace was used for annealing the tensile specimens.