Part I – January 1969 - Papers - Experimental Analysis of Deformation Twin Behavior in Embrittled Iron-Chromium Alloys: Part III

A study co.mbining stress-strain .measurements in conjunction with transmission electron microscoPy has been made with near equiatomic Fe-Cr alloys which were aged for various times at 500°C. Associated with this aging is a marked increase in deformation twinning. The outstanding feature of these twins is that they generate stress fields sufficiently great so as to give rise to spontaneous dislocation loop nucleation nearly normal to the propagating twin. This observation is in agreement with the theoretically predicted elongation of the stress field of a dislocation Perpendicular to its direction of motion as it moves near the speed of sound. Dislocation loop nucleation is more difficult in the longer aged alloys so that this energy absorption mechanism is not effective in hindering twin propagation. Since crack nucleation can readily occur near the tip of a twin, the aged alloys become extremely brittle when deformed in tension. Iron-chromium alloys in the vicinity of the equiatomic compositions become severely embrittled when aged at about 500°C. Fisher et 01.' have shown that this embrittlement is related to the decomposition of the original random Fe-Cr solid solution into a chromium-rich and an iron-rich phase. In addition, Mar-cinkowski et a1.' have shown that twinning becomes an increasingly more important mode of deformation as the aging time is increased. These results have been recently corroborated by the transmission electron microscopy study of Mima and amauchi . The Fe-Cr alloy thus seems ideal for verifying the predictions made in Parts I4 and 115 of this investigation where the behavior of large static or blocked twins and those of large dynamic or propagating twins, respectively, were investigated numerically. It was thus decided to measure the stress-strain curves generated by embrittled alloys that were aged for various times and to examine sections by transmission electron microscopy. EXPERIMENTAL PROCEDURE Electrolytic iron and electrolytic chromium were vacuum-melted and poured into ingot form. The composition of the resulting alloy was found to contain 46.0 wt pct Cr (47.8 at. pct), the remainder being iron. The resulting ingot was swaged above 850°C into 0.250-and 0.400-in.-diam rounds. Compression samples of 0.250 in. diam and 0.400 in. long were cut from the smaller-diameter rounds. These samples were then sealed in evacuated quartz tubes and annealed for 30 min at 1150°C to produce a uniform and equiaxed grain size of mean diameter equal to 1.73 mm. They in turn were rapidly quenched from 850°C so as to preserve the condition of random solid-solution characteristic of the elevated temperature. The samples were then aged for various times up to 300 hr at 500°C in a massive Pb-Bi alloy bath. The samples were next polished and tested in compression at room temperature as described in Ref. 6 using an Instron tensile testing machine. The strain rate used was 0.05 in. per in. per min. The remaining larger round was converted into compression specimens of 0.325 in. diam and 0.500 in. long. This larger diameter enabled wafers of sufficient size to be prepared for examination by trans-mission electron microscopy techniques after subjecting them to a suitable strain. Foil preparation is described in some detail in Ref. 6. All foils were examined in a type HU-11A Hitachi electron microscope operating at 100 kv. RESULTS AND DISCUSSION Fig. 1 shows the effect of aging at 500°C on the room-temperature stress-strain curves of the FeCr alloys. For greater clarity the origin of each curve has been displaced upward. The same origin has been used for both the 0 and the 0.1 curves. It is apparent that with increased aging times a sharp drop in load is observed at the yield stress which becomes more pronounced as aging proceeds. A loud sonic burst accompanies this drop and subsequent metallographic examination shows the sample to contain numerous twins. For intermediate aging times, a number of smaller twin bursts follow the initial large one. The total plastic strain associated with the twinning mode of deformation can be obtained by adding up the contributions AE~ from all i twin bursts, i.e., £,¦££,-, in the manner illustrated schematically in Fig. 2. The contraction of the specimen, as measured from the strip chart of the Instron, after suitably correcting for the elasticity of the machine, was converted into true strain using the assumption that there was no volume change and that the sample remained cylindrical. The dashed lines are all drawn parallel to the