Pilot Trial of Detoxification of Chromium Slag in Cyclone Furnace and Preparation of Glass-Ceramics with the Water-Quenched Melt

Pilot trial ofthe detoxification ofchromium slag in cyclonefurnace and the preparation of glass-ceramics were investigated in a power plant in China. 10wt.%chromiumslagweremixedwithpulverizedbituminouscoalandlimestone as the raw materials of the cyclone furnace. Cr(VI) in chromium slag was reduced toCr O insidethecyclonefurnace.Themeltwaswater-quenchedintofritandthen 2 3 fired into glass-ceramics with a laboratory ceramicrollerkiln. The preparation and crystallization behavior of glass-ceramics were investigated with differential ther- mal analysis (DTA), physical and mechanical properties testing, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The optimal flexural strength exceeding 90 MPa were achieved in firing temperature zone of 1170–1200 °C. Anorthite (CaAl Si O ) and diopside [Ca(Mg, Fe)Si O ] can be identified in the 2 2 8 2 6 glass-ceramicsandCaAl Si O isthepredominantcrystalphase.Fineparticleswith 2 2 8 average diameter of 200 nm distributed uniformly in the glass-ceramics. Granular crystals are intensively interconnected and constituted a crystal skeleton soaked in theglassmatrix.LeachingtoxicitytestdetectedCr(VI)of0.016and0.010 mg/Lof the water-quenched frit and glass-ceramics, respectively. This method provides an effective and comprehensive technique for the detoxification and utilization of chromium slag at low cost and large-scale. (cid:1) (cid:1)