Pre-Oxidation And Hydrogen Reduction Of Panzhihua Ilmenite Concentrate

The reduction degree and rate of the initial ilmenite concentrate and pre-oxidation samples by hydrogen were investigated by using thermogravimetric analysis system. H2-TPR was used to detected reduction properties of the pre-oxidation products which were oxidized at different temperatures. The phase transformations and micromorphology changes during pre-oxidation and hydrogen reduction were identified by XRD and SEM. The FeTiO3 was decomposed into TiO2 and Fe2O3 at the temperature below 900 oC. With the temperature rising, Fe2TiO5 was the only stable phase in high temperatures. The reduction of pre-oxidation ilmenite concentrate was faster than the natural sample, which was attributed to the micropores generated on the surface of ilmenite concentrate during oxidation. The main phases of the reduction product were metallic iron, ferrous pseuodbrookite.