Premature ageing of a blast furnace taphole clay containing resole resin and liquid pitch as binder

The cause of reduced workability and increased ageing of a blast furnace taphole clay was examined. The investigated taphole clay contained 60 mass% alumina, with phenol-formaldehyde resole resin and liquid pitch serving as the binder system. The workability and Marshall extrusion pressure of the as-manufactured clay samples were evaluated to assess the extent of ageing of the clay. The wettability of all the raw materials was investigated to confirm compatibility between the dry raw materials and both the resin and liquid pitch, while the dry raw materials were analysed using XRF, XRD, and SEM-EDS. The characterisation of the resin and liquid pitch, as well as an analysis of their interaction, was performed using viscosity measurements, Fouriertransform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). The analyses confirmed a chemical interaction between the resole resin and liquid pitch, where the chemical structure of the resole resin changed when mixed with pitch, preventing the typical curing behaviour of the resin. Upon ageing of the resin-pitch mixtures, the resin underwent premature cross-linking, causing the curing process to initiate at lower temperatures, i.e., earlier onset of curing. This premature cross-linking was likely due to secondary amines present in the liquid pitch, which acted as a catalyst for the curing process of the resin. This reduction in curing temperature after ageing was confirmed by an increase in binder viscosity, which was identified as the primary cause of reduced workability, accelerated ageing, and increased Marshall extrusion pressure of the taphole clay.