Preparation of Nano Gold Powder from an Acid Leaching Tail Solution

According to the unique properties and many applications of nano gold powder, it was prepared from an acid leaching tail solution. The low value residual gold ions were existed in acid leaching tail solution in Mouteh gold mine in Iran with fellow heavy metals as pollutants (FeP2+P, Cu P2+P, and ZnP2+P). Preparation of nano gold particles is achieved by two steps. First, by addition of ammonia as separation step and second using suitable reagents for precipitation/extraction step. Conditions control includes pH, residence time, temperature, agitation, and molar ratio of reducing agents to reagents. The optimum results show that nano gold powder was prepared by temperature of 250 °C, urea to gold molar ratio of 3:1, and reduction time of 20 min. Also, heat treatment improves dispersion of nano sized gold particles. The properties of gold nano powders were evaluated by SEM, A.A, and UV- Vis spectroscopy methods. The size of prepared particles were about 80nm to 90nm.