Preparation of SCR Catalyst Carrier by APCVD and Sol-Gel Technologies

"TiO2 has been loaded on cordierite porous ceramic to prepare the SCR catalyst carrier by using both APCVD and sol-gel technology. In APCVD method, TiC14 and O 2 were used as reaction precursor. TiC14 was gasified by using N2 as carrier gas which was controlled to 500sccm. Its reaction temperature and reaction time were limited to 773K and 30min respectively. The physical properties, SEM and SEM-EDX of the TiO2-cordierite carrier and the properties of SCR catalysts prepared by these carriers have been tested. The tests showed that TiO2 loaded by APCVD method were of graininess shape and even accumulation. The loading rate of TiO2 and the specific area of carrier sample were increased 114% and 21 % respectively comparing with sol-gel technology. In the result of sol-gel method, the maximal difference of Ti content was 66.92%, while the result of APCVD method was 18.89%. It demonstrated that TiO2 was uniformly attached with the cordierite ceramic by using APCVD method, which would ensure more active ingredients well loaded on the Ti02-cordierite carrier. This difference made the denitrification ratio of catalyst prepared by APCVD method was 8.1 % higher than that of catalyst prepared by sol-gel method.IntroductionIn recent years, the emission of NOx, which were caused by coal-fired power plants, has gotten more and more attention. SCR (selective catalytic reduction) is the most effective technology to DeNOx [ll. The core technology of it is the catalyst. The SCR catalyst usually uses Ti02 as the carrier, and V2O 5 as the active component [2, 3] . However, the thermal stability and mechanical properties of TiO2 carrier are unstable, which would influence the performances of the catalyst. The commercial catalyst generally uses WO3 or MoO3 to promote its heat stability at present [4-7] Besides, TiO2 is expensive. Compared with TiO2, the cordierite is of good thermal stability and lower price. So loading Ti02 on cordierite porous ceramic as carrier to produce SCR catalyst is of good prospects [S, 91 • Currently, TiO2 is usually loaded on cordierite by the sol-gel method. But some research has shown that the sol-gel method easily reduced the loading performances of TiO2, such as distribution, combination, etc. APCVD (atmospheric pressure chemical vapor deposition) has many advantages to preparing TiO2 films, such as high bonding strength, fast reaction rate and so on [l0-13l_ In this paper, TiO2 has been loaded on cordierite porous ceramic to prepare the SCR catalyst carrier by using both APCVD and sol-gel methods. The properties of the carriers prepared by the two processes have also been compared."