Preparation Of The Solution Containing Metal Nano-Particles And Its Characterization

We prepared the water dispersed with Au particles ranging from 10 to 20 nm size by a novel wet chemical synthesis; generating seeds of Au cluster by adding a borane dimethylamine complex into chloroaureic acid (gold salt) solution, and then growing simultaneously with aminoalcohol included in the solution. As-prepared Au nano-particles with chemical surface modification were found to have some attractive performances, i.e., showing a high dispersiveness in an aqueous solution in a long time, sintering nano-particles at low temperature, and having low resistivity in the film prepared from nano-particles. In the case that smaller Au nano-particles were removed from as-prepared colloid, especially, Au thin film formed on the surface of Si plate showed the excellent value of 7.0x10-6ohm cm (reference peculiar resistance: 2.35x10-6 ohm cm).The sintering temperature was dependent on the elimination of 2-aminoethanol that modified on the surface of Au nano-particles.