Pressure Oxidation Leaching Of Gold-Antimony Alloy

Au-Sb alloy sample in which the total amount of Cu and Ni is below 25% (wt. %). In practice, Cu and Ni were difficult to be dissolved in sulphuric acid solution by oxidative leaching under the atmospheric pressure conditions, because of the lower concentration of Cu and Ni in the sample. In this paper, pressure oxidation leaching in sulphuric acid system (POLS) followed by hydrochloric acid leaching (HAL) was employed to remove impurities in the Au-Sb alloy. The effects of variables in POLS on leaching ratios of different metals were investigated in detail. Under the optimal conditions: the concentration of H2SO4 is 1.5 mol/L, liquid-solid ratio is 7:1, the amount of oxidizer is 1.2 times of the theoretical amount, leaching time is 4h and leaching temperature is 427K, the leaching ratios of copper and nickel reached up to 99%, antimony, lead and silver were not dissolved in dilute sulphuric acid solution. The residue from POLS was then treated with hydrochloric acid solution in fixed conditions, the leaching ratio of antimony reached over 92%, the grade of gold in the ultima residue was enriched up to 66%.