Pressure Oxidation Pyrometallurgical Technology of Gold-Bearing and Lead and Zinc Sulfide Concentrates Undergoing Combined Treatment

The pressure oxidation (POX) and pyrometallurgical process comprises POX of gold containing sulfide and polymetallic lead-zinc concentrates prior to reduction smelting of POX products to generate a lead-silver-gold alloy. Refined lead and gold-silver alloys are then obtained using conventional processes. Zinc and other base metals are recovered from the POX solution. In the course of POX, zinc dissolves in the solution and lead concentrates in a solid residue in the form of sulfate compounds. Sulfur forms the major iron sulfates and jarosites. In order to dissolve sulfur and arsenic from solid residues to the solution, the slurry hot curing was carried out at the temperature of 95°C within 2 hours. After filtration of the slurry, zinc was recovered from the solution. The resulting cake was washed with water and subjected to hot alkaline treatment. After alkaline treatment, the cakes were blended with fluxes and subjected to reduction smelting to generate lead concentrate containing precious metals. This concentrate was refined to obtain refined lead and gold-silver alloy. After iron and arsenic were removed from POX solutions using sodium carbonate, zinc was precipitated as carbonate. After thickening and filtration, zinc precipitate was roasted to generate saleable zinc oxide. Using this process, the recoveries of values to saleable products were 97% Au and 95% Ag to the alloy, respectively, 91% Pb to refined lead and 5% Pb to lead and antimony alloy and 94% Zn to zinc concentrate. The features of the technology is that it has high recovery indices of precious and base metals to saleable products and can be used to process various polymetallic ore and technogenic raw materials.