Process and Practice of Reducing the Cr Loss during EAF with De-P Hot Metal Charging Melting Stainless Steel

"The article introduces the process EAF with De-P hot metal charging for Melting Stainless Steel in Baosteel stainless steel Branch. Based on the practice of production, the main effect on the Cr Loss during EAF with De-P Hot Metal Charging Melting Stainless Steel including using oxygen, the material charging and making slag are theoretically analyzed. The optimization of using oxygen can reduce the oxidation of Cr during EAF Melting Stainless Steel. The optimization of material charging, especially Si content is suitable can reduce the loss of Cr. Effective reduction can realize the lowest Cr oxide in slag. Based on the character of the process EAF with De-P hot metal charging for Melting Stainless Steel, applied the integrated control method, the Cr loss during EAF melting stainless steel decreased 43.10%. 1 INTRODUCTION EAF with De-P HM charging for melting stainless steel is a technology for stainless steel making. Practice prove that the new process can shorten tap to tap time, reduce the special power consumption, dilute the impurity element from the stainless steel scrap that is propitious to produce the high quality stainless steel, alleviate the shortage of stainless steel scrap to the production. As a new technology, the process has some technical problems and difficulties. The proportion of Cr alloy charging exceeds 20% during EAF with De-P hot metal charging melting stainless steel. As Cr alloy is difficult melting and easy oxidation, too much Cr alloy charging result in Cr loss too much and tap to tap time too long for EAF production. By applying the new technology, Baosteel stainless steel branch has increased the technology level and economy index. Now the content of Cr oxide in slag reduce from 8.59% to less than 6.0%. The Cr loss during EAF melting stainless steel decreased 43.10%. According to the practice application, the process of EAF with De-P HM melting stainless steel are theoretically analyzed. The main factors affecting the Cr loss during EAF with De-P hot metal charging melting stainless steel are discussed."