Production of NbAl3 Powders through Sodium Reduction of Oxides in Molten Salts

"Na2NbAlO5 was synthesized using Nb2O5 and NaAlO2 as raw materials in molten NaCl-CaCl2 by a solid reaction. With an addition of sodium into the melts, Na2NbAlO5 was subsequently reduced to form NbAl3 intermetallic compound with a particle size of 50-300nm.IntroductionThe intermetallic compounds of niobium aluminides have been a subject of research interests as high temperature materials because of their properties such as high melting temperature, large specific strength at elevated temperature, good resistance to high temperature oxidation, low density and large ductility [1,2]. They are applicable for turbine blades in aircraft engines and stationary gas turbines [3,4].In recent years, the methods of powder synthesis have been widely discussed. There are many methods to synthesis intermetallic compounds such as conventional melting and solidification [5], powder metallurgy [6,7], reaction sintering [8] and reaction sintering with prior mechanical activation [9,10]. There is a prominent weakness in such methods that they use metal to produce intermetallic compounds by the means of diffusion reaction. Although the metal can diffusion sufficiently, it is still hard to avoid maldistribution of the constituents which impairs the properties of the materials."