Pseudo-Binary Phase Diagram of the Cuspidine-CaF2 System-Relating to Mold Flux for Continuous Casting of Steel

The pseudo-binary phase diagram of the cuspidine (3CaO2?SiO2?CaF2) - CaF2 system has been studied by electron probe microanalysis (EPMA) and X-ray diffractometry (XRD). To prevent fluorine loss in the form of a HF gas by a reaction of CaF2 with water vapor at elevated temperatures, the equilibrium experiments were conducted with the sample hermetically sealed in a platinum tube. By employing this technique, it was successfully revealed that cuspidine exists as a stable phase and congruently melts at 1684 ± 1 K, and the cuspidine - CaF2 system presents a simple eutectic type of phase diagram, of which eutectic temperature has been estimated to be around 1540 K, corresponding to the composition of 40 mass% 3CaO?2SiO2 - 60 mass% CaF2?