Reaction Between Mno-Sio₂ Oxides With Low Feo Content And Solid Steel Deoxidized By Si And Mn During Heat Treatment

In order to clarify the reaction between MnO-SiO2 oxides with low FeO content and Fe-Mn-Si alloy, two diffusion couples were produced by the new method using confocal scanning laser microscopy (CSLM). The interface of the alloy and oxide, content of Mn and Si in the alloy near the interface, size distribution and composition of the particles which precipitated in the alloy were observed and analyzed using the electron probe microanalysis (EPMA). Results show that though the FeO content in the oxides decrease to 1% which is lower than the equilibrium with the molten steel at 1873K, the diffusion of oxygen from oxide to alloy still exists during the heat treatment at 1473K and causes shorter Particle Precipitated Zone (PPZ) and Manganese Depleted Zone (MDZ) normally for the reduction of diffusion flux of oxygen.