Recovery of alcohol after anti-solvent precipitation of (NH4)3ScF6 from NH4F strip liquors, E.M. Peters, Ş. Kaya, C. Dittrich, M. Svärd, and K. Forsberg

Scandium can be recovered from waste streams of other metallurgical processes such as red mud from the Bayer process and titanium dioxide acid waste. This is accomplished by an integrated process comprising leaching using acidic media, solvent extraction using organic solvents and stripping of Sc from the organic phase using NH4F solutions. The precipitation of scandium as (NH4)3ScF6 from NH4F strip liquors has been demonstrated at lab-scale with recoveries and purities greater than 98% and 98.3%, respectively. It is desired to assess the possibility of recovering the solvents for re-use in the process to improve its economy and environmental friendliness. Investigations have been conducted to recover alcohol by simple distillation from strip liquor-alcohol mixtures containing about 50 v/v% alcohol. The mixtures were obtained after anti-solvent precipitation of (NH4)3ScF6 using an alcohol to strip liquor volumetric ratio of 1:1. The starting strip liquor contained about 2000 mg/L scandium in 3 mol/L NH4F solution. In the recovery of methanol, the first distillate product collected had a purity of about 87 v/v% and this decreased slightly with time over two hours. The methanol distillate collected in the first 30 minutes with a purity of ca. 85 v/v% was re-used in anti-solvent crystallisation of (NH4)3ScF6 from the initial strip liquor, and the scandium recovery attained was about 98.6 w/w%, almost similar to that of 99.2 w/w% obtained using 100 v/v% methanol. For ethanol recovery, the first distillate product collected was approx. 84 v/v% pure and the distillate collected in the first 30 minutes with a purity of about 75 v/v% achieved a scandium recovery of about 97.2 w/w% in comparison to 98.5 w/w% obtained using 100 v/v% ethanol during anti-solvent crystallisation. Keywords: Alcohol recovery, methanol, ethanol, anti-solvent crystallisation, (NH4)3ScF6